8.8 HOT DIP GALV STUD M10X150
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these ar..
8.8 HOT DIP GALV STUD M10X90
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are ..
8.8 HOT DIP GALV STUD M12X160
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these ar..
8.8 HOT DIP GALV STUD M20X280
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these ar..
8.8 HOT DIP GALV STUD M24X210
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these ar..
EN8 HOT DIP GALV STUD M8X130
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are ei..