Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are..
EN8 ELECTRO GALV STUD M20X240
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are..
8.8 ELECTRO GALV STUD M24X210
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are..
EN8 HOT DIP GALV STUD M10X150
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are..
EN8 HOT DIP GALV STUD M10X90
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are ..
EN8 HOT DIP GALV STUD M12X110
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are e..
8.8 HOT DIP GALV STUD M12X150
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these ar..
EN8 HOT DIP GALV STUD M16X125
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are e..
EN8 HOT DIP GALV STUD M16X190
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are e..
8.8 HOT DIP GALV STUD M12X170
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these ar..
EN8 HOT DIP GALV STUD M20X170
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are e..
EN8 HOT DIP GALV STUD M20X240
Explaining the difference between EN8 and 8.8 steel as indicted
8.8 is ISO 898–1 grading for Bolts and screws. It indicates a bolt/screw with
tensile strength of minimum 800MPa and a yield strength of 80% of 800MPa = 640MPa.
Depending on thickness these are e..